Improved production process of light burned magnesia balls

Improvement of the production process of light burnt magnesia balls

The preparation of light burnt magnesia ball is to add 80% light burnt magnesia powder into 2O water, put it into a mill for rolling, stirring, and magnesia carbon brick manufacturer to mix for 15～20min to form a mixture, and send it to press ball mechanism through belt conveyor Prepare the products and stack them. The finished product of light-burned magnesia ball is ready for sale after being dried in the shade for 48 hours and forming strength.

The necessity of improving the production process of light burnt magnesia balls

The light-burned magnesia ball product is produced according to the above preparation process, and the quality of the product has the following problems

1) Low ball formation rate. After the raw materials are processed by the ball press, half are products and half are powder particles. The powder particles need to be manually returned to the ball press machine for further processing.

Continue processing.

2) The sphere is loose. The density is small, the strength is low, and it is easily broken. Especially during loading and unloading, transportation, squeezing and falling, the sphere is prone to breakage.

3) The shape of the sphere is not complete. Some are half-balls, some are thirds, and some have missing corners, different shapes, and matte surfaces.

The appearance image is poor.

4) The user is not satisfied. The products sold contain 20%-35% of small pieces and powders and other mixed materials, and users have repeatedly raised objections to this.